ASTM E2751-12
Standard Practice for Design and Performance of Supported Laminated Glass Walkways
Standard Practice for Design and Performance of Supported Laminated Glass Walkways
E2751-12
ASTM|E2751-12|en-US
Standard Practice for Design and Performance of Supported Laminated Glass Walkways
Standard
E2751 Standard Practice for Design and Performance of Supported Laminated Glass Walkways>
new
BOS Vol. 04.12 Committee E06
$
77.00
In stock
Significance and Use
4.1 Glass is a brittle material with different time and temperature-dependent properties than other solid materials used as walkways surfaces. Therefore, the type of glass is an important consideration in the design and construction of glass treads and glass landings constructed with laminated glass.
4.2 Post-breakage glass retention is an important consideration in the design of a glass walkway system as a means of minimizing tripping, cutting/piercing injuries, or fall-through or fallout of the glass.
4.3 The structural design shall be confirmed by calculations by a licensed design professional in accordance with Section 5.
4.4 If testing is required (see 4.4.1-4.4.3) to verify post-glass breakage behavior of the glass walkway, the testing shall be in accordance with Section 6.
4.4.2 For laminates with more than two glass plies, verification testing is not required provided that calculations completed in accordance with 4.3 demonstrate that the glass assembly has sufficient strength to sustain the full design load with any one glass ply broken.
4.4.3 When verifying post-breakage behavior by calculation, allowable glass stress for 10 min load duration in accordance with Table 1 shall be used for all load cases.
TABLE 1 Allowable Glass Stresses for Nominal Load Conditions
Note 1—An allowable stress reduction factor of 0.5 is recommended for disruptive surface treatments, for example, acid etching or sandblasting, unless otherwise provided by the manufacturer. A glass stress reduction factor may be required for some patterned glasses; consult the manufacturer.
Note 2—Values derived from Practice E1300, Table X9.1 (seamed edges), factored for load duration using Practice E1300, Equation X7.1, using n = 16 for annealed glass, n = 32 for heat strengthened glass, and n = 48 for tempered glass.
| Glass Type | 3-sec | 10-min | 60-min | Permanent |
| Annealed | 18.3 (2650) | 13.2 (1902) | 11.7 (1701) | 5.7 (827) |
| Heat-strengthened | 36.5 (5300) | 30.9 (4482) | 29.2 (4235) | 20.3 (2944) |
| Tempered | 73.0 (10 600) | 65.3 (9471) | 63.0 (9137) | 49.4 (7165) |
4.5 The manufacturer or designer of glass walkway systems shall provide installation directions and fabrication and installation tolerances of their systems.
4.6 The structural integrity of the glass walkway system after glass breakage shall be sufficient to support the design loads after any one glass ply is broken. If damage of any kind occurs, the walkway shall be cordoned off and the installation shall be inspected to ensure structural integrity and pedestrian safety of the system.
Scope
1.1 This practice addresses elements related to load-bearing glass walkways, glass treads, and glass landings constructed with laminated glass. This standard includes performance, design, and safe behavior considerations. It addresses the characteristics unique to glass and laminated glass. Issues that are common to all walkways, such as slip resistance, are addressed in existing referenced standards.
1.2 This practice does not address glass walkways constructed with monolithic glass, glass block, insulating glass units, glass tiles that are directly bonded to a non-glass structural substrate, or glass walkways intended to support vehicular traffic.