ASTM C607-88(2024)
Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
C0607-88R24
ASTM|C0607-88R24|en-US
Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
Standard
C607 Standard Practice for Coking Large Shapes of Carbon-Bearing Materials>
new
BOS Vol. 15.01 Committee C08
$
64.00
In stock
ASTM International
Significance and Use
3.1 This practice is useful for preparing coked specimens for subsequent testing where the shapes desired cannot be fitted into the coking box described in Test Methods C831.
3.2 This practice can be very sensitive to heating rates in coking. Thus, strict adherence to the coking procedure is necessary.
Scope
1.1 This practice covers the preparation of coking of carbon-bearing material for subsequent testing such as modulus of rupture, slag testing, thermal conductivity, and thermal expansion. Test Methods C831 is the specified method for testing residual carbon.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.