Standard Historical Last Updated: Aug 21, 2013 Track Document

ASTM B241/B241M-12

Standard Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded Tube

Standard Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded Tube B0241_B0241M-12 ASTM|B0241_B0241M-12|en-US Standard Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded Tube Standard B241/B241M Standard Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded Tube> new BOS Vol. 02.02 Committee B07

$ 91.00 In stock

Abstract

This specification covers aluminum and aluminum-alloy seamless pipe and seamless extruded tube. The pipe and tube shall be produced from hollow extrusion ingot (cast in hollow form, or drilled, or pierced from solid ingot) and shall be extruded by use of the die and mandrel method. The material shall conform to the chemical composition requirements specified. The determination of chemical composition shall be made in accordance with suitable chemical (test methods E 34) or spectrochemical (test methods E 227, E 607, and E 1251) methods. Alloys may be solution heat-treated and quenched at the extrusion press in accordance with practice B 807 for the production of T4 and T6-type tempers, as applicable. The material shall conform to the tensile property requirements specified. The tension tests shall be made in accordance with test methods B 557. The stress-corrosion cracking test shall be performed on extruded tube. The stress-corrosion test shall be made in accordance with test method G 47. The aluminum alloy coating of clad tube shall comprise the inside surface (only) of the tube and its thickness shall be approximately 10 % of the total wall thickness of the tube.

Scope

1.1 This specification² covers aluminum and aluminum–alloy seamless pipe in the alloys (Note 1) and tempers shown in Table 1 [Table 2] and seamless extruded round tube in the alloys and tempers shown in Table 3 [Table 4] intended for pressure applications. The standard sizes for seamless pipe are listed in Table 16.7 of ANSI H35.2 and H35.2M . Nonstandard alloys, tempers, and sizes of pipe are produced as seamless extruded tube.

TABLE 1 Tensile Property Limits for Pipe, Inch-Pound Units^A^,^B

Alloy	Temper	Pipe Size, in.	Tensile Strength, min, ksi	Yield Strength (0.2 % Offset), min, ksi	Elongation in 2 in. or 4 × Diameter, min, %^C
3003	H18	Under 1	27.0	24.0	4
	H112	1 and over	14.0	5.0	25
6005	T1	All	25.0	15.0	16
	T5	All	38.0	35.0	8
6005A	T1	All	25.0	14.5	15
	T5	All	38.0	31.0	7
	T61	Under 0.250	38.0	35.0	8
		0.250-1.000	38.0	35.0	10

6041	T6	All	45.0	40.0	10
6042	T5, T5511	All	38.0	35.0	10
6061	T6 (Extruded)	Under 1	38.0	35.0	8
		1 and over	38.0	35.0	10^D
	T6 (Drawn)	Under 1	42.0	35.0	8^E
		1 and over	38.0	35.0	10^F
6063	T6	All	30.0	25.0	8
6064	T6	All	42.0	38.0	10
6082	T6	All	45.0	38.0	8
6105	T1	All	25.0	15.0	16
	T5	All	38.0	35.0	8
6262	T6	All	38.0	35.0	10
6351	T5	All	38.0	35.0	10^D
	T6	All	42.0	37.0	10^G

^A The basis for establishment of tensile property limits is shown in Annex A1.

^B For purposes of determining conformance with this specification, each value for tensile strength and yield strength shall be rounded to the nearest 0.1 ksi, and each value for elongation shall be rounded to the nearest 0.5 %, both in accordance with the rounding-off method of Practice E29.

^C Elongation of full-section and cut-out sheet-type specimens is measured in 2 in.; of round specimens, in 4 × specimen diameter.

^D For wall thicknesses less than 0.250 in., the minimum elongation is 8 %.

^E For wall thickness 0.050 to 0.259 in., the minimum elongation is 10 %.

^F For wall thickness 0.260 to 0.500 in., the minimum elongation is 12 %.

^G For wall thickness less than 0.125 in., the minimum elongation is 8 %.

TABLE 2 Tensile Property Limits for Pipe [SI Units]^A^,^B

Alloy	Temper (Product)	Pipe Size, Designation	Tensile Strength, min, MPa	Yield Strength (0.2 % Offset), min, MPa	Elongation,^C min, %
Alloy	Temper (Product)	Pipe Size, Designation	Tensile Strength, min, MPa	Yield Strength (0.2 % Offset), min, MPa	in 50 mm	in 5 × Diameter
3003	H18	Under 1	185	165	4	...
	H112	1 and over	95	35	25	22
6005	T1	All	170	105	16	14
	T5	All	260	240	8
6005A	T1	All	170	100	15
	T5	All	260	215	7	6
	T61	All	260	240	8
6041	T6	All	310	275	10	9
6042	T5, T5511	All	260	240	10	9
6061	T6 (Extruded)	Under 1	260	240	8	...
		1 and over	260	240	10^D	9
	T6 (Drawn)	Under 1	290	240	8^E	...
		1 and over	260	240	10^F	9
6063	T6	All	205	170	8	7
6064	T6	All	290	260	10	9
6082	T6	All	310	260	10	8
6105	T5	All	260	240	8	7
	T6	All	290	255	10	9
6262	T6	All	260	240	10	9
6351	T5	All	260	240	10^D	9
	T6	All	290	255	10^G	9

^A The basis for establishment of mechanical property limits is shown in Annex A1.

^B For purposes of determining conformance with this specification, each value for ultimate strength and yield strength shall be rounded to the nearest 1 MPa, and each value for elongation shall be rounded to the nearest 0.5 %, both in accordance with the rounding-off method of Practice E29.

^C Elongations in 50 mm apply for pipe tested in full-section and to sheet type specimens taken from pipes having a wall up to 12.50 mm thick. Elongations in 5D

Equation B0241_B0241M-12_2

where D and A are diameter and cross-sectional area of the specimens respectively, apply to round test specimens machined from wall thicknesses over 6.30 mm.

^D For wall thicknesses up through 6.30 mm the minimum elongation is 8 %.

^E For wall thicknesses over 1.25 through 6.60 mm, the minimum elongation is 10 %.

^F For wall thicknesses over 6.60 through 12.50 mm, the minimum elongation is 12 %.

^G For wall thicknesses up through 3.20 mm the minimum elongation is 8 %.

TABLE 3 Tensile Property Limits for Extruded Tube, Inch-Pound Units^A^,^B


Temper	Specified Section or Wall Thickness, in.	Area, in.²	Tensile Strength, ksi		Yield Strength (0.2 % Offset), ksi		Elongation in 2 in. or 4 × Diameter, min, %^C
			Min	Max	Min	Max
Aluminum 1060
O	all	all	8.5	14.0	2.5	. . .	25
H112	all	all	8.5	. . .	2.5	. . .	25
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Aluminum 1100
O	all	all	11.0	15.5	3.0	. . .	25
H112	all	all	11.0	. . .	3.0	. . .	25
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 2014
O	all	all	. . .	30.0	. . .	18.0	12
T4
T4510^E	all	all	50.0	. . .	35.0	. . .	12
T4511^E

T42	all	all	50.0	. . .	29.0	. . .	12

T6	up thru 0.499	all	60.0	. . .	53.0	. . .	7
T6510^E	0.500–0.749	all	64.0	. . .	58.0	. . .	7
T6511^E	0.750 and over	up thru 25	68.0	. . .	60.0	. . .	7
		over 25 thru 32	68.0	. . .	58.0	. . .	6

T62	up thru 0.749	all	60.0	. . .	53.0	. . .	7
	0.750 and over	up thru 25	60.0	. . .	53.0	. . .	7
		over 25 thru 32	60.0	. . .	53.0	. . .	6
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 2024
O	all	all	. . .	35.0	. . .	19.0	12

T3	up thru 0.249	all	57.0	. . .	42.0	. . .	10
T3510^E	0.250–0.749	all	60.0	. . .	44.0	. . .	10
T3511^E	0.750–1.499	all	65.0	. . .	46.0	. . .	10
	1.500 and over	up thru 25	70.0	. . .	48.0	. . .	10
		over 25 thru 32	68.0	. . .	46.0	. . .	8

T42	up thru 0.749	all	57.0	. . .	38.0	. . .	12
	0.750–1.499	all	57.0	. . .	38.0	. . .	10
	1.500 and over	up thru 25	57.0	. . .	38.0	. . .	10
		over 25 thru 32	57.0	. . .	38.0	. . .	8

T81	0.050–0.249	all	64.0	. . .	56.0	. . .	4
T8510^E	0.250–1.499	all	66.0	. . .	58.0	. . .	5
T8511^E	1.500 and over	up thru 32	66.0	. . .	58.0	. . .	5
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 2219
O	all	all	. . .	32.0	. . .	18.0	12

T31
T3510^E	up thru 0.499	up thru 25	42.0	. . .	26.0	. . .	14
T3511^E	0.500–2.999	up thru 25	45.0	. . .	27.0	. . .	14

T62	Up thru 0.999	up thru 25	54.0	. . .	36.0	. . .	6
	1.000 and over	up thru 25	54.0	. . .	36.0	. . .	6

T81
T8510^E	up thru 2.999	up thru 25	58.0	. . .	42.0	. . .	6
T8511^E
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 3003
O	all	all	14.0	19.0	5.0	. . .	25
H112	all	all	14.0	. . .	5.0	. . .	25
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alclad Alloy 3003
O	all	all	13.0	18.0	4.5	. . .	25
H112	all	all	13.0	. . .	4.5	. . .	25
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 5052
O	all	all	25.0	35.0	10.0	. . .	. . .
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 5083
O	all	up thru 32	39.0	51.0	16.0	. . .	14
H111	all	up thru 32	40.0	. . .	24.0	. . .	12
H112	all	up thru 32	39.0	. . .	16.0	. . .	12
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 5086
O	all	up thru 32	35.0	46.0	14.0	. . .	14
H111	all	up thru 32	36.0	. . .	21.0	. . .	12
H112	all	up thru 32	35.0	. . .	14.0	. . .	12
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 5154
0	all	all	30.0	41.0	11.0		. . .
H112	all	all	30.0	. . .	11.0		. . .
Alloy 5454
O	all	up thru 32	31.0	41.0	12.0	. . .	14
H111	all	up thru 32	33.0	. . .	19.0	. . .	12
H112	all	up thru 32	31.0	. . .	12.0	. . .	12
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 5456
O	all	up thru 32	41.0	53.0	19.0	. . .	14
H111	all	up thru 32	42.0	. . .	26.0	. . .	12
H112	all	up thru 32	41.0	. . .	19.0	. . .	12
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 6005
T1	Up thru 0.500	all	25.0		15.0		16
T5	Up thru 0.124	all	38.0		35.0		8
	0.125–1.000	all	38.0		35.0		10
Alloy 6005A
T1	Up thru 0.249	all	25.0		14.5		15
T5	Up thru 0.249	all	38.0		31.0		7
	0.250–0.999	all	38.0		31.0		9
T61	Up thru 0.249	all	38.0		35.0		8
	0.250–1.000	all	38.0		35.0		10
Alloy 6013
T6, T6511	0.200-0.499	all	49.0		46.0		8
	0.500-0.749	all	49.0		46.0		8
	0.750-2.000	all	49.0		45.0		8
Alloy 6041
T6, T6511	0.400–2.000	all	45.0		40.0		10
Alloy 6042
T5, T5511	0.400–0.499	all	38.0		35.0		10
	0.500–1.800	all	42.0		35.0		10
Alloy 6061
O	all	all	. . .	22.0	. . .	16.0	16

T1	up thru 0.625	all	26.0	. . .	14.0	. . .	16

T4
T4510^E	all	all	26.0	. . .	16.0	. . .	16
T4511^E

T42	all	all	26.0	. . .	12.0	. . .	16

T51	up thru 0.625	all	35.0	. . .	30.0	. . .	8

T6, T62
T6510^E	up thru 0.249	all	38.0	. . .	35.0	. . .	8
T6511^E	0.250 and over	all	38.0	. . .	35.0	. . .	10
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 6063
O	all	all	. . .	19.0	. . .	. . .	18

T1^F	up thru 0.500	all	17.0	. . .	9.0	. . .	12
	0.501–1.000	all	16.0	. . .	8.0	. . .	12

T4, T42	up through 0.500	all	19.0	. . .	10.0	. . .	14
	0.501–1.000	all	18.0	. . .	9.0	. . .	14

T5	up thru 0.500	all	22.0	. . .	16.0	. . .	8
	0.501–1.000	all	21.0	. . .	15.0	. . .	8

T52	up thru 1.000	all	22.0	30.0	16.0	25.0	8

T6, T62	up thru 0.124	all	30.0	. . .	25.0	. . .	8
	0.125–1.000	all	30.0	. . .	25.0	. . .	10
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 6064
T6, T6511	0.400–2.000	all	42.0		38.0		10
Alloy 6066
O	all	all	. . .	29.0	. . .	18.0	16
T4,
T4510^E	all	all	40.0	. . .	25.0	. . .	14
T4511^E

T42	all	all	40.0	. . .	24.0	. . .	14

T6,
T6510,^E	all	all	50.0	. . .	45.0	. . .	8
T6511^E

T62	all	all	50.0	. . .	42.0	. . .	8
Alloy 6082
T6	0.200–1.000	all	45.0		38.0		8
Alloy 6105
T1	Up thru 0.500	all	25.0		15.0		16
T5	Up thru 0.500	all	38.0		35.0		8
Alloy 6162
T5,
T5510^E	up thru 1.000	all	37.0	. . .	34.0	. . .	7
T5511^E

T6,
T6510^E	up thru 0.249	all	38.0	. . .	35.0	. . .	8
T6511^E	0.250–0.499	all	38.0	. . .	35.0	. . .	10
Alloy 6262
T6, T6511	all	all	38.0		35.0		10
Alloy 6351
T4	up thru 0.749	all	32.0	. . .	19.0	. . .	16
T6	up thru 0.124	. . .	42.0	. . .	37.0	. . .	8
	0.125–0749	. . .	42.0	. . .	37.0	. . .	10
Alloy 7075
O	all	. . .	. . .	40.0	. . .	24.0	10

T6, T62	up through 0.249	all	78.0	. . .	70.0	. . .	7
T6510^E	0.250–0.499	all	81.0	. . .	73.0	. . .	7
T6511^E	0.500–1.499	all	81.0	. . .	72.0	. . .	7
	1.500–2.999	all	81.0	. . .	72.0	. . .	7

T73	0.062–0.249	all	68.0	. . .	58.0	. . .	7
T73510	0.250–1.499	up thru 25	70.0	. . .	61.0	. . .	8
T73511	1.500–2.999	up thru 25	69.0	. . .	59.0	. . .	8
F^D	all	all	. . .	. . .	. . .	. . .	. . .
Alloy 7178
O	all	up thru 32	. . .	40.0	. . .	24.0	10

	up through 0.061	all	82.0	. . .	76.0	. . .	. . .
	0.062–0.249	up thru 20	84.0	. . .	76.0	. . .	5
T6	0.250–1.499	up thru 25	87.0	. . .	78.0	. . .	5
T6510^E	1.500–2.499	up thru 25	86.0	. . .	77.0	. . .	5
T6511^E		over 25 thru 32	84.0	. . .	75.0	. . .	5
	2.500–2.999	up thru 32	82.0	. . .	71.0	. . .	5

T62	up thru 0.061	all	79.0	. . .	73.0	. . .	. . .
	0.062–0.249	up thru 20	82.0	. . .	74.0	. . .	5
	0.250–1.499	up thru 25	86.0	. . .	77.0	. . .	5
	1.500–2.499	up thru 25	86.0	. . .	77.0	. . .	5
		over 25 thru 32	84.0	. . .	75.0	. . .	5
	2.500–2.999	up through 32	82.0	. . .	71.0	. . .	7
F^D	all	all	. . .	. . .	. . .	. . .	. . .

^A The basis for establishment of mechanical property limits is shown in Annex A1.

^B To determine conformance to this specification, each value for ultimate strength and for yield strength shall be rounded to the nearest 0.1 ksi and each value for elongation to the nearest 0.5 %, both in accordance with the rounding-off-method of Practice E29.

^C Elongation of full-section and cut-out sheet-type specimens is measured in 2 in.; of round specimens, in 4 × specimen diameter. See 9.1.1 for conditions under which measurements are not required.

^D Tests for tensile properties in the F temper are not required.

^E For stress relieved tempers (T3510, T3511, T4510, T4511, T5510, T5511, T6510, T6511, T73510, T73511, T8510, T8511), characteristics and properties other than those specified may differ somewhat from the corresponding characteristics and properties of material in the basic tempers.

^F Formerly designated T42 temper. When properly aged (precipitation heat-treated) 6063-T1 extruded products are designated T5.

TABLE 4 Tensile Property Limits for Extruded Tube [SI Units]^A^,^B


Temper	Specified Section or Wall Thickness, mm			Area, mm²		Tensile Strength, MPa		Yield Strength (0.2 % offset), MPa		Elongation,^C %, min
Temper		over	through	over	through	min	max	min	max	in 50 mm	in 5 × diameter
Aluminum 1060
O		all		all		60	95	15	. . .	25	22
H112		all		all		60	. . .	15	. . .	25	22
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Aluminum 1100
O		all		all		75	105	20	. . .	25	22
H112		all		all		75	. . .	20	. . .	25	22
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 2014
O		all		all		. . .	205	. . .	125	12	10

T4		all		all		345	. . .	240	. . .	12	10
T4510^E
T4511^E

T42^F		all		all		345	. . .	200	. . .	12	10

T6		. . .	12.50	all		415	. . .	365	. . .	7	6
T6510^E		12.50	18.00	all		440	. . .	400	. . .	. . .	6
T6511^E		18.00	. . .	. . .	16 000	470	. . .	415	. . .	. . .	6
		18.00	. . .	16 000	20 000	470	. . .	400	. . .	. . .	5

		. . .	18.00	all	. . .	415	. . .	365	. . .	7	6
		18.00	. . .	. . .	16 000	415	. . .	365	. . .	. . .	6
T62^F		18.00	. . .	16 000	20 000	415	. . .	365	. . .	. . .	5

F^D		all		all	. . .	. . .	. . .	. . .	. . .	. . .	. . .
Alloy 2024
O		all		all		. . .	240	. . .	130	12	10

T3		. . .	6.30	all		395	. . .	290	. . .	10	. . .
T3510^E		6.30	18.00	all		415	. . .	305	. . .	10	9^H
T3511^E		18.00	35.00	all		450	. . .	315	. . .	. . .	9
		35.00	. . .	. . .	16 000	485	. . .	330	. . .	. . .	9
		35.00	. . .	16 000	20 000	470	. . .	315	. . .	. . .	7

		. . .	18.00	all	. . .	395	. . .	260	. . .	12	10
		18.00	35.00	all		395	. . .	260	. . .	. . .	9
T42^F		35.00	. . .	. . .	16 000	395	. . .	260	. . .	. . .	9
		35.00	. . .	16 000	20 000	395	. . .	260	. . .	. . .	7

T81		1.20	6.30	all		440	. . .	385	. . .	4	. . .
T8510^E		6.30	35.00	all		455	. . .	400	. . .	5	4
T8511^E		35.00	. . .	. . .	20 000	455	. . .	400	. . .	. . .	4

F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 2219
O		all		all		. . .	220	. . .	125	12	10

T31		. . .	12.50	. . .	16 000	290	. . .	180	. . .	14	12
T3510^E		12.50	80.00		16 000	310	. . .	185	. . .	. . .	12
T3511^E

		. . .	25.00	. . .	16 000	370	. . .	250	. . .	6	5
T62^F		25.00		. . .	20 000	370	. . .	250	. . .	. . .	5

T81
T8510^E		. . .	80.00	. . .	16 000	400	. . .	290	. . .	6	5
T8511^E

F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 3003
O		all	. . .	all		95	130	35	. . .	25	22

H112		. . .	1.60	all		95	. . .	35	. . .	. . .	. . .
		1.60	. . .	all		95	. . .	35	. . .	25	22
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alclad Alloy 3003
O		all		all		90	125	30	. . .	25	22
H112		all		all		90	. . .	30	. . .	25	22
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 5052
O		all		all		170	240	70	. . .	. . .	. . .
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 5083
O		all		. . .	20 000	270	350	110	. . .	14	12
H111		all		. . .	20 000	275	. . .	165	. . .	12	10
H112		all		. . .	20 000	270	. . .	110	. . .	12	10
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 5086
O		all		. . .	20 000	240	315	95	. . .	14	12
H111		all		. . .	20 000	250	. . .	145	. . .	12	10
H112		all		. . .	20 000	240	. . .	95	. . .	12	10
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 5154
0		all		all		205	285	75			. . .
H112		all		all		205	. . .	75			. . .
Alloy 5454
O		all		. . .	20 000	215	285	85	. . .	14	12
H111		all		. . .	20 000	230	. . .	130	. . .	12	10
H112		all		. . .	20 000	215	. . .	85	. . .	12	10
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 5456
O		all		. . .	20 000	285	365	130	. . .	14	12
H111		all		. . .	20 000	290	. . .	180	. . .	12	10
H112		all		. . .	20 000	285	. . .	130	. . .	12	10
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 6005
T1		. . .	12.50	all		170	. . .	105	. . .	16	14
T5		. . .	3.20			260	. . .	240	. . .	8	. . .
		3.20	25.00			260	. . .	240	. . .	10	9
Alloy 6005A
T1		. . .	6.30	all		170	. . .	100	. . .	15
T5		. . .	6.30	all		260	. . .	215	. . .	7
		6.30	25.00	all		260	. . .	215	. . .	9	8
T61		. . .	6.30	all		260	. . .	240	. . .	8
		6.30	25.00	all		260	. . .	240	. . .	10	9
Alloy 6013
T6, T6511		5.00	12.50	all		340		315		8	. . .
		12.50	20.00	all		340		315		. . .	7
		20.00	50.00			340		310		. . .	7

Alloy 6041
T6, T6511		10.00	50.00			310	. . .	275	. . .	10	9
Alloy 6042
T5, T5511		10.00	12.50	all		260	. . .	240	. . .	10
		12.50	50.00	all		290	. . .	240	. . .		9
Alloy 6061
O		all		all		. . .	150	. . .	110	16	14

T1		. . .	16.00	all		180	. . .	95	. . .	16	14

T4				all		180	. . .	110	. . .	16	14
T4510^E		all
T4511^E

T42^F		all		all		180	. . .	85	. . .	16	14

T51		. . .	16.00	all		240	. . .	205	. . .	8	7

T6, T62^F		. . .	6.30	all		260	. . .	240	. . .	8	. . .
T6510^E		6.30	. . .	all		260	. . .	240	. . .	10	9
T6511^E

F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 6063
O		all		all		. . .	130	. . .	. . .	18	16

T1		. . .	12.50	all	. . .	115	. . .	60	. . .	12	10
		12.50	25.00	all	. . .	110	. . .	55	. . .	. . .	10

T4,T42^F		. . .	12.50	all		130	. . .	70	. . .	14	12
		12.50	25.00	all		125	. . .	60	. . .	. . .	12

T5		. . .	12.50	all		150	. . .	110	. . .	8	7
		12.50	25.00	all		145	. . .	105	. . .	. . .	7

T52		. . .	25.00	all		150	205	110	170	8	7

T6		. . .	3.20	all		205	. . .	170	. . .	8	. . .
		3.20	25.00	all		205	. . .	170	. . .	10	9

F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 6064
T6, T6511		10.00	50.00			290		240		10	9
Alloy 6066
O		all		all		. . .	200	. . .	125	16	14
T4,
T4510^E		all		all		275	. . .	170	. . .	14	12
T4511^E

T42		all		all		275	. . .	165	. . .	14	12
T6,
T6510^E		all		all		345	. . .	310	. . .	8	7
T6511^E

T62		all		all		345	. . .	290	. . .	8	7
Alloy 6082
T6		5.00	25.00			310		260		8	10^G
Alloy 6105
T1		. . .	12.50	all		170	. . .	105	. . .	16	14
T5		. . .	12.50	all		260	. . .	240	. . .	8	7
Alloy 6162
T5,
T5510^E		. . .	25.00	all		255	. . .	235	. . .	7	6
T5511^E

T6,		. . .	6.30	all		260	. . .	240	. . .	8	. . .
T6510^E		6.30	12.50	all		260	. . .	240	. . .	10	9
T6511^E

Alloy 6262
T6, T6511		all		all		260	. . .	240	. . .	10	9
Alloy 6351
T4		. . .	20.00	all		220	. . .	130	. . .	16	14
T6		. . .	3.20	. . .		290	. . .	255	. . .	8
		3.20	25.00	. . .		290	. . .	255	. . .	10	9
Alloy 7075
O		all		all		. . .	275	. . .	165	10	9

T6, T62^F		. . .	6.30	all		540	. . .	485	. . .	7	. . .
T62510^E		6.30	12.50	all		560	. . .	505	. . .	7	6
T6511^E		12.50	70.00	all		560	. . .	495	. . .	. . .	6

T73		1.60	6.30	all	13 000	470	. . .	400	. . .	7
T73510^E		6.30	35.00		16 000	485		420		8	7
		35.00	70.00		16 000	475		405			7
T73511^E
F^D		all		all		. . .	. . .	. . .	. . .	. . .	. . .
Alloy 7178
O		all		. . .	20 000	. . .	275	. . .	165	10	9

		. . .	1.60	all		565	. . .	525	. . .	. . .	. . .
		1.60	6.30	. . .	13 000	580	. . .	525	. . .	5	. . .
T6		6.30	35.00	. . .	16 000	600	. . .	540	. . .	5	4
T6510^E		35.00	60.00	. . .	16 000	595	. . .	530	. . .	. . .	4
T6511^E		35.00	60.00	16 000	20 000	580	. . .	515	. . .	. . .	4
		60.00	80.00	. . .	20 000	565	. . .	490	. . .	. . .	4

		. . .	1.60	all	13 000	545	. . .	505	. . .	. . .	. . .
		1.60	6.30	. . .	13 000	565	. . .	510	. . .	5	. . .
		6.30	35.00	. . .	16 000	595	. . .	530	. . .	5	4
T62^F		35.00	60.00	. . .	16 000	595	. . .	530	. . .	. . .	4
		35.00	60.00	16 000	20 000	580	. . .	515	. . .	. . .	4
		60.00	80.00	. . .	20 000	565	. . .	490	. . .	. . .	4

F^D		all	all		. . .	. . .	. . .	. . .	. . .	. . .

^A The basis for establishment of tensile property limits is shown in Annex A1.

^B To determine conformance to this specification, each value for tensile strength and yield strength shall be rounded to the nearest 1 MPa and each value for elongation to the nearest 0.5 %, both in accordance with the rounding-off method of Practice E29.

^C Elongation in 50 mm apply for shapes tested in full section and for sheet-type specimens machined from material up through 12.5 mm in thickness having parallel surfaces. Elongations in 5 D

Equation B0241_B0241M-12_48

where D and A are diameter and cross-sectional area of the specimen respectively, apply to round test specimens machined from thicknesses over 6.30. See 9.1.1 for conditions under which measurements are not required.

^D No mechanical properties are specified or guaranteed.

^E For stress-relieved tempers (T3510, T3511, T4510, T4511, T5510, T5511, T6510, T6511, T73510, T73511, T76510, T76511, T8510, T8511), characteristics and properties offer than those specified may differ somewhat from the corresponding characteristics and properties of material in the basic tempers.

^F Material in the T42 and T62 tempers is not available from the material producers.

^G For Table 12.1 in both ASD and ASD(M):

For purposes of harmonization, the 5D and 50 mm elongation limits were established to match extruded tube elongation values previously published in EN 755-2 [1997]. The relationship among the US customary and metric elongation values does not comply with the conversion rules of the Aluminum Association.

Note 1—Throughout this specification, use of the term alloy, in the general sense, includes aluminum as well as aluminum alloy.

Note 2—For other seamless drawn tubes, see Specification B210 or Specification B483/B483M. For extruded tube see Specification B221, and for structural pipe and tube see Specification B429/B429M.

1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1M . The equivalent Unified Numbering System alloy designations are those of Table 5preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527.

1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.4.1 The SI units are shown either in brackets or in separate tables.

Version

Language

Format

Price:

Shipping & Handling

ASTM License Agreement

Reprints and Permissions

Reprints and copyright permissions can be requested through the
Copyright Clearance Center

Details

Book of Standards Volume: 02.02

Developed by Subcommittee: B07.03

Pages: 20

DOI: 10.1520/B0241_B0241M-12

ICS Code: 77.150.10

Order Total	Shipping & Handling Fee
Up to $50.00	$18.00
$50.01 to $100.00	$20.00
$100.01 to $150.00	$28.38
$150.01 to $250.00	$37.59
$250.01 to $500.00	$54.09
$500.01 to $750.00	$73.48
$750.01 to $1000.00	$89.57
$1000.01 to $1500.00	$116.61
$1500.01 to $2500.00	$152.29
$2500.01 to $4999.00	$201.00
$5000.00 to $higher	$225.00

Standard Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded Tube