Standard
Historical
Last Updated: Dec 31, 2010
Track Document
ASTM A958-00(2006)
Standard Specification for Steel Castings, Carbon and Alloy, with Tensile Requirements, Chemical Requirements Similar to Standard Wrought Grades
Standard Specification for Steel Castings, Carbon and Alloy, with Tensile Requirements, Chemical Requirements Similar to Standard Wrought Grades
A0958-00R06
ASTM|A0958-00R06|en-US
Standard Specification for Steel Castings, Carbon and Alloy, with Tensile Requirements, Chemical Requirements Similar to Standard Wrought Grades
Standard
A958 Standard Specification for Steel Castings, Carbon and Alloy, with Tensile Requirements, Chemical Requirements Similar to Standard Wrought Grades>
new
BOS Vol. 01.02 Committee A01
$
86.00
In stock
Abstract
This specification covers carbon and low-alloy steel castings. The steel specimens shall be heat treated and shall conform to the required values of austenitizing temperature and tempering temperature. The steel materials shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, and molybdenum. Tensile tests shall be performed and the steel specimens shall conform to the required values of tensile strength, yield strength, and elongation.
Scope
1.1 This specification covers carbon and low-alloy steel castings having chemical analyses similar to that of the standard wrought grades.
1.2 Several classes are covered and are designated by chemical composition as shown in .
1.3 Options for tensile properties are shown in .
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. Inch-pound units are applicable for material ordered to Specification A 958 and SI units for material ordered to Specification A 958.