ASTM A660-96(2010)
Standard Specification for Centrifugally Cast Carbon Steel Pipe for High-Temperature Service
Standard Specification for Centrifugally Cast Carbon Steel Pipe for High-Temperature Service
A0660-96R10
ASTM|A0660-96R10|en-US
Standard Specification for Centrifugally Cast Carbon Steel Pipe for High-Temperature Service
Standard
A660 Standard Specification for Centrifugally Cast Carbon Steel Pipe for High-Temperature Service>
new
BOS Vol. 01.02 Committee A01
$
77.00
In stock
Abstract
This specification covers carbon steel pipe made by the centrifugal casting process intended for use in high-temperature, high-pressure service. This pipe shall be suitable for fusion welding, bending, and other forming operations. Grades for carbon steels shall conform to the required chemical composition for carbon, manganese, phosphorous, sulfur, and silicon. Manufacturing of the material shall be done by machining and heat treatment. Pyrometers shall be used to control the furnace temperatures. Tensile properties shall conform to the required values for tensile strength, elongation, and reduction of area. Mechanical properties shall conform to the following: transverse or longitudinal tension test; flattening test; and hydrostatic test.
Scope
1.1 This specification covers carbon steel pipe made by the centrifugal casting process intended for use in high-temperature, high-pressure service. Pipe ordered under this specification shall be suitable for fusion welding, bending, and other forming operations.
1.2 Several grades of carbon steels are covered. Their compositions are given in Table 1.
1.3 Supplementary requirements (S1 to S9) of an optional nature are provided. The supplementary requirements call for additional tests to be made, and when desired shall be so stated in the order, together with the number of such tests required.
1.4 The values stated in inch-pound units are to be regarded as the standard.