ASTM A451/A451M-06(2010)
Standard Specification for Centrifugally Cast Austenitic Steel Pipe for High-Temperature Service
Standard Specification for Centrifugally Cast Austenitic Steel Pipe for High-Temperature Service
A0451_A0451M-06R10
ASTM|A0451_A0451M-06R10|en-US
Standard Specification for Centrifugally Cast Austenitic Steel Pipe for High-Temperature Service
Standard
A451/A451M Standard Specification for Centrifugally Cast Austenitic Steel Pipe for High-Temperature Service>
new
BOS Vol. 01.01,01.02 Committee A01
$
77.00
In stock
Abstract
This specification covers the standard for centrifugally cast austenitic alloy steel pipe for use in high-temperature, corrosive, or nuclear pressure service. The pipe shall receive a heat treatment at the required temperature and holding time followed by quenching in water or rapid cool by other means. The pipe shall be machined on the inner and outer surfaces and shall conform to specified roughness value. Heat and product analysis shall be done to determine the chemical composition and shall conform to the required carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, molybdenum, columbium, tantalum, and nitrogen contents. Hydrostatic and tension tests shall be performed and shall conform to the required tensile strength, yield strength, and elongation.
Scope
1.1 This specification covers austenitic alloy steel pipe for use in high-temperature, corrosive, or nuclear pressure service.
1.2 Several grades of austenitic stainless steel are covered as indicated in Table 1.
1.3 Optional supplementary requirements are provided when additional testing may be required.