Ion Damage in 316 Stainless Steel Over a Broad Dose Range

Source

Microstructural evolution was examined in annealed 316 stainless steel after heavy-ion bombardment in the range 1 to 256 dpa at 900 K with simultaneously implanted helium at a rate of 10 appm/dpa and deuterium at a rate of 25 appm/dpa. Phase decomposition was rather limited compared with that in neutron irradiations; only an unidentified plate-like precipitate at low dose, and blocky M2 3C6 particles on grain boundaries were formed. Swelling from cavity formation increased with dose to about 20% at about 200 dpa above which it appeared to saturate. Cavity concentrations saturated at about 100 dpa, and dislocations much earlier. The matrix cavities included a persistant complement of ∼7-nm diam small cavities. Similar-size helium bubbles were prolific on the grain boundaries.

Author Information

Packan, NH
Oak Ridge National Laboratory, Oak Ridge, TN
Farrell, K
Oak Ridge National Laboratory, Oak Ridge, TN
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: E10
Pages: 885–894
DOI: 10.1520/STP34385S
ISBN-EB: 978-0-8031-4846-8
ISBN-13: 978-0-8031-0753-3