Influence of Cold Work on the Irradiation Creep and Creep Rupture of Titanium Modified Austenitic Stainless Steel
SourceA titanium-modified austenitic type stainless steel was tested at three cold work levels to determine its creep and creep rupture properties under both thermal aging and neutron irradiation conditions. Both the thermal and irradiation creep behavior exhibit a complex non-monotonic relationship with cold work level that reflects the competition between a number of stress-sensitive and temperature dependent microstructural processes. Increasing the degree of cold work to 30% from the conventional 20% level was detrimental to its performance, especially for applications above 550°C. The 20% cold work level is preferable to the 10% level, in terms of both in-reactor creep rupture response and initial strength.
Author Information
Garner, FA
Battelle Pacific Northwest Laboratories, Richland, Washington
Hamilton, ML
Battelle Pacific Northwest Laboratories, Richland, Washington
Eiholzer, CR
Westinghouse Hanford Company, Richland, Washington
Toloczko, MB
University of California at Santa Barbara, Santa Barbara, CA
Kumar, AS
Materials Research Center, University of Missouri, Rolla, Rolla, MO
Related
Reprints and Permissions
Details
Developed by Committee: E10
Pages: 696–713
DOI: 10.1520/STP23967S
ISBN-EB: 978-0-8031-5262-5
ISBN-13: 978-0-8031-1488-3