Mechanism-Based Variability in Fatigue Life of Ti-6Al-2Sn-4Zr-6Mo
SourceThe variability in fatigue life of a Ti-6Al-2Sn-4Zr-6Mo alloy was studied. The cumulative life distribution plot was found to be composed of two distinct failure mechanisms, designated as Type-I and Type-II. The likelihood of Type-I vs. Type-II failure shifted with respect to the stress level, such that at lower stress levels, there was increased probability of Type-II failure. It also was found that the variability in life was introduced primarily at the crack nucleation stage, specifically, formation of a stage-I crack across an equiaxed primary-α particle.
Author Information
Jha, SK
Systran Federal Corporation, Dayton, OH
Larsen, JM
Air Force Research Laboratory, Materials and Manufacturing Directorate, AFRL/MLLMN, Wright Patterson AFB, Dayton, OH
Rosenberger, AH
Air Force Research Laboratory, Materials and Manufacturing Directorate, AFRL/MLLMN, Wright Patterson AFB, Dayton, OH
Hartman, GA
The University of Dayton Research Institute, Dayton, OH
Related
Reprints and Permissions
Details
Developed by Committee: E08
Pages: 116–127
DOI: 10.1520/STP11283S
ISBN-EB: 978-0-8031-5496-4
ISBN-13: 978-0-8031-3478-2