Microstructural Characteristics of Sand Asphalt Mortar

CODEN: JTEVAB

Abstract

Fine aggregate matrix (FAM), an intermediate scale of asphalt concrete (AC), helps identify how small-scale mixture components affect overall AC-scale mechanical behavior. However, investigating FAM does not straightforwardly identify the influence of asphalt binders on AC fatigue behavior due to fine aggregates mixed in FAM. To address this limitation and minimize the variability caused by different fine aggregates, some researchers propose using sand asphalt mortar (SAM) to exclusively focus on the binder effect. To better represent binder characteristics using SAM, it is critical to identify the correct binder amount and its volumetric characteristics. This study aims to perform an in-depth evaluation of SAM microstructural characteristics, specifically air void (AV) and binder film thickness (FT). Thus, six SAM samples, fabricated with Ottawa sand and two types of asphalt binder at three contents (6 %, 8 %, and 10 %) were produced in cylindrical bars. Furthermore, one FAM mixture derived from its AC mixture was also evaluated for comparison. To assess location-dependent microstructural characteristics, the samples were cut into three parts (top, middle, and bottom), which were examined for measuring AV and FT. Test results showed that average AV and median FT were the best parameters to consider. SAM specimens were homogeneous in terms of FT for any content or asphalt binder type; however, in terms of AV, homogeneity was only observed at a 6 % binder content. It is noted that FT values were smaller than 60 µm from both SAM and FAM samples, which is significantly lower than the thickness used at parallel plate geometry (i.e., 1–2 mm thick) in typical rheological tests. These findings indicate that SAM is considered a reasonable mix to effectively characterize binder behavior in AC mixtures due to its realistic film geometry, which is significant for understanding the effects of binder on viscoelastic mechanical properties in AC mixtures.

Author Information

Curado, Tallyta da Silva
Federal Institute of Education, Science and Technology of Goiás, Jataí, GO, Brazil
de Rezende, Lilian Ribeiro
School of Civil Engineering, Federal University of Goiás, Goiânia, GO, Brazil
Teixeira, Jamilla Emi Sudo Lutif
Department of Civil and Environmental Engineering, College of Engineering, University of Nebraska-Lincoln, Lincoln, NE, USA
Kim, Yong-Rak
Zachry Department of Civil and Environmental Engineering, Texas A&M University, College Station, TX, USA
Pages: 22
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: JTE20240470
ISSN: 0090-3973
DOI: 10.1520/JTE20240470