ASTM C216-13
Standard Specification for Facing Brick (Solid Masonry Units Made from Clay or Shale)
Standard Specification for Facing Brick (Solid Masonry Units Made from Clay or Shale)
C0216-13
ASTM|C0216-13|en-US
Standard Specification for Facing Brick (Solid Masonry Units Made from Clay or Shale)
Standard
C216 Standard Specification for Facing Brick (Solid Masonry Units Made from Clay or Shale)>
new
BOS Vol. 04.05 Committee C15
$
96.00
In stock
Abstract
This specification covers brick intended for use in masonry and supplying structural or facing components, or both, to the structure. Bricks shall be classified according to their resistance to damage by freezing when saturated at a moisture content: Grade SW and Grade MW. The facing bricks shall be classified into three types: Types FBS; FBX; and FBA. Durability; absorption alternate; freezing and thawing alternative; breakage and weight loss; cracking; low weathering index alternative; compressive strength; and initial rate of absorption requirements shall be tested for the material to meet the specified requirements.
Scope
1.1 This specification covers brick intended for use in masonry and supplying structural or facing components, or both, to the structure.
1.2 The property requirements of this specification apply at the time of purchase. The use of results from testing of brick extracted from masonry structures for determining conformance or nonconformance to the property requirements (Section 7) of this specification is beyond the scope of this specification.
1.3 The brick are prismatic units available in a variety of sizes, textures, colors, and shapes. This specification is not intended to provide specifications for paving brick (see Specification C902).
1.4 Brick are ceramic products manufactured primarily from clay, shale, or similar naturally occurring earthy substances and subjected to a heat treatment at elevated temperatures (firing). Additives or recycled materials are permitted to be included at the option of the manufacturer. The heat treatment must develop a fired bond between the particulate constituents to provide the strength and durability requirements of this specification (see Terminology C1232).
1.5 Brick are shaped during manufacture by molding, pressing, or extrusion, and the shaping method is a way to describe the brick.