ASTM A678/A678M-05(2009)
Standard Specification for Quenched-and-Tempered Carbon and High-Strength Low-Alloy Structural Steel Plates (Withdrawn 2010)
Standard Specification for Quenched-and-Tempered Carbon and High-Strength Low-Alloy Structural Steel Plates (Withdrawn 2010)
A0678_A0678M-05R09
ASTM|A0678_A0678M-05R09|en-US
Standard Specification for Quenched-and-Tempered Carbon and High-Strength Low-Alloy Structural Steel Plates (Withdrawn 2010)
Standard
A678/A678M Standard Specification for Quenched-and-Tempered Carbon and High-Strength Low-Alloy Structural Steel Plates (Withdrawn 2010)>
new
BOS Vol. 01.04 Committee A01
$
0.00
Out of stock
Abstract
This specification covers quenched-and-tempered carbon steel and high-strength low-alloy steel plates of structural quality for welded, riveted, or bolted construction. The plates shall undergo heat treatment by heating to a temperature that produces an austenitic structure. Heat and product analyses shall be performed on the material and shall conform to the required amount of chemical composition in carbon, manganese, phosphorus, sulfur, silicon, vanadium, columbium, nitrogen, and copper. The plates shall withstand tension test and applicable grade shall conform to the specified mechanical properties such as yield strength, tensile strength, and elongation.
Scope
1.1 This specification covers quenched-and-tempered carbon steel and high-strength low-alloy steel plates of structural quality for welded, riveted, or bolted construction.
1.2 If the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be used.
1.3 Plates under this specification are available in four grades as follows:
| Grade | Yield Strength, min, ksi [MPa] | Tensile Strength, ksi [MPa] | Maximum Thickness, in. [mm] |
| A | 50 [345] | 70–90 [485–620] | 11/2 [40] |
| B | 60 [415] | 80–100 [550–690] | 21/2 [65] |
| C | A | A | 2 [50] |
| D | 75 [515] | 90–110 [620–760] | 3 [75] |
A Varies with thickness. See Table 1.
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be used independently of the other.